Alumina Zirconia P-Grit Abrasive Grain is Zirconia abrasive material for coated abrasive tools. It always goes ZA40 P-Grit.
Zirconia Alumina is made of high-purity alumina and zirconium material as raw materials. After high temperature smelting at 2700℃, it is formed by special processing technology and Barmac ball milling. It has high quality, extremely hard, compact structure, and special crystals. Dendritic eutectic structure. According to the content of ZrO2, zirconia alumina can be divided into ZA25 Zirconia alumina (ZrO225%) and ZA40 Zirconia alumina(ZrO2 40%).
Zirconia alumina is different from ordinary fused alumina and silicon carbide with superior self-sharpening, toughness, and wear resistance. Used for making grinding wheels, it can significantly improve the life and sharpness of grinding wheels, and for grinding and cutting workpieces with higher hardness, the wear resistance is particularly obvious. Mainly used for the production of heavy-duty grinding wheels, resin-bonded grinding wheels, cutting discs, wear-resistant products, high-grade abrasive tools, etc., Zirconia Alumina is suitable for grinding steel parts, cast iron parts, heat-resistant steel, titanium alloys, nickel alloys, aluminum alloys, tungsten titanium alloys and other materials. The grinding ability is higher than that of ordinary abrasive materials.
The characteristics of zirconia alumina:
- The toughness of Zirconia is very high, about 13-15 times that of brown aluminum oxide.
- The crystal size of zirconia is very small (HAIXU ordinary quality crystal size is 18-20um, HAIXU high-quality crystal size is 10-12um), which is one twentieth of the ordinary electron fused alumina. The smaller crystal size can continuously produce small sharpness edges during grinding. So the service life is improved.
- The bulk density of zirconia is high (1.9-2.45g/cm3), while the bulk density of ordinary fused corundum such as white aluminum oxide and brown aluminum oxide is 1.55-1.95g/cm3. Zirconia alumina is suitable for the production of high-speed grinding wheels, heavy-duty grinding wheels, and cutting discs and other abrasive tools.
The difference between ZA25 and ZA40:
l ZA25 has a higher alumina content than ZA40, which is suitable for wear-resistant products such as wear-resistant hammers, heavy-duty grinding wheels, bonded abrasive tools, etc.
l The self-sharpening, hardness and toughness of ZA40 are better than ZA25, suitable for cutting discs, railway cutting & grinding wheel, high-level resin grinding wheels, coated abrasives, etc.
| Chemical Content | ||
| Item | ZA25 | ZA40 |
| AL2O3 | 70-72% | 55-57% |
| ZrO2 | 24-30% | 35-44% |
| TiO2 | Max 1.0% | Max 0.8% |
| Fe2O3 | Max 0.3% | Max 0.25% |
| SiO2 | Max 0.8% | Max 0.6% |
| Physical Properties | ||
| Item | ZA25 | ZA40 |
| Specific Gravity | 4.30g/cm3 | 4.60g/cm3 |
| Bulk Density | 1.90-2.30g/cm3 | 2.15-2.45g/cm3 |
| Knoop Hardness | 1600 | 1450 |
| Smelting Point | 1950℃ | 1900℃ |
| Crystal shape | monoclinical tetragonal | |
| Chemical property | Amphoteric | |
| Reaction with acid and alkali | No | |
| Reaction with carbon | Forming carbide since 1650 ℃ | |
| Crystal Size | HXB Series18-20um，HXA Series 10-12um | |
| Maximum service temperature | 1600 ℃ | |
| Color | Gray | |
| Specific heat capacity(cal/g.C) | 0.2205(50-500℃) | |
| Heat conductivity | 0.2718 cal/cm2.sec.℃ | |
| Linear expansivity(X10-6) | 6.82(100-700℃) | |
Available Sizes：
| F-Grit(For bonded abrasive tools) | 6# 8# 10# 12# 14# 16# 20# 22# 24# 30# 36# 40# 46# 54# 60# 70# 80# 90# 100# 120# 150# 180# 220# |
| P-Grit(For coated abrasive tools) | 24# 30# 36# 46# 54#60# 70# 80# 90# 100# 120# 150# 180# 220# |
| Section sand and finer powder(For refractory) | 0-0.5mm,0-1mm,1-3mm,3-5mm,5-8mm,100#-0,200#-0,320#-0 |
Applications:
- Used to produce heavy-duty grinding wheels, tough grinding wheels, and high-level resin-bonded grinding wheels.
- Used for grinding and cutting hard-to- grind materials.
- Used for high-quality cutting discs, grinding discs, polishing wheels, etc.
- Used to produce coated abrasives, such as sandpaper, abrasive belts, flexible polishing wheels, fiber disc, nylon polishing wheel etc. It can improve polishing accuracy and work efficiency.
- Used in the production of wear-resistant hammers and linings.
- Used for sandblasting, suitable for marble, super-hard steel, steel castings and other materials.
- Used for high-level refractory materials, such as castables, intrusive nozzles, sliding nozzles, etc.